耐蚀合金冷轧带 GB/T15012—1994
众钢网 2009-04-23 16:41:32
(1)尺寸规格见表8-52。
表8-52耐热合金冷轧带的尺寸规格 (mm)
厚度及
厚度允
许偏差 |
宽度
厚度 |
厚度允许偏差 |
20~150 |
>150~250 |
>250~400 |
>400~630 |
0.02~O.10 |
±O.008 |
±O.010 |
±O.OlO |
|
>0.10~0.15 |
±0.010 |
±0.010 |
±O.OlO |
|
>O.15~O.25 |
±O.015 |
±0.015 |
±O.015 |
±0.020 |
>O.25~O.45 |
±O.020 |
±0.020 |
±O.020 |
±O.025 |
>O.45~0.65 |
±O.O25 |
±0.025 |
±0.025 |
±O.030 |
>O.65~O.90 |
±O.030 |
±0.030 |
±0.030 |
±0.040 |
>0.90~1.20 |
±0.035 |
±O.040 |
±O.040 |
±O.045 |
>1.20~1.50 |
±O.045 |
±O.050 |
±O.050 |
±O.055 |
>1.50~1.80 |
±0.06 |
±0.065 |
±0.065 |
±O.07 |
>1.80~2.00 |
±O.06 |
±0.07 |
±0.075 |
±O.08 |
>2.00~2.30 |
±O.07 |
士O.08 |
±0.08 |
士0.09 |
>2.30~2.50 |
±O.07 |
土O.08 |
±0.08 |
±0.09 |
>2.50~3.10 |
±O.08 |
±O.09 |
±O.09 |
±O.10 |
>3.10~4.00 |
±O.09 |
±O.10 |
±O.10 |
±0.11 |
宽度及宽度允
许偏差 |
宽度边缘状态 |
宽度允许偏差 |
20~50 |
>50~150 |
>150~250 |
>250~400 |
>400~630 |
切边带材 |
+l.O
O |
+2.O
O |
+3.0
0 |
+4.0
0 |
+5.0
0 |
不切边带材 |
+2
-l |
+3
-2 |
+6
-2 |
+7
-3 |
+20
O |
注:1.切边带材的镰刀弯应符合下列规定:
宽度20—50mm带材,每米长度不大于3mm;宽度大于50mm带材,每米长度不大于2mm。
2.根据需方要求,可以把表中厚度的正负偏差改为正偏差或负偏差,但此时的公差值应与表中规定的公差值相等。
(2)力学性能见表8-53。
表8-53耐蚀合金冷轧带的力学性能
合金牌号 |
状态 |
抗拉强度ób/MPa |
屈服强度ó0.2/MPa |
伸长率δ5(%) |
硬度 |
≥ |
NS111
NS112 |
退火 |
520 |
205 |
30 |
— |
NS142 |
退火 |
585 |
240 |
30 |
≤95HRB |
NS311 |
固溶 |
570 |
245 |
45 |
— |
1/2H |
805 |
— |
10 |
— |
NS312
NS315 |
退火 |
505 |
240 |
30 |
— |
1/4H |
— |
— |
— |
88~94HRB |
1/2H |
— |
— |
— |
93~98HRB |
3/4H |
— |
— |
— |
97HRB~25HRC |
H |
860 |
620 |
2 |
— |
NS321 |
退火 |
795 |
345 |
45 |
100HRB① |
NS322 |
退火 |
760 |
350 |
40 |
100HRB① |
NS333 |
固溶 |
690 |
315 |
30 |
— |
NS336 |
退火 |
830 |
415 |
30 |
— |
固溶 |
690 |
275 |
30 |
— |
注:1.屈服强度值,仅当需方要求时(在合同中注明)才测定。
2.屈服强度要求不适用于厚度小于0.50mm的带材。
3.厚度小于0.25mm的带材不作拉力试验,但应提供硬度数据。
①硬度值仅供参考。